Effect of cathodic potential on stress corrosion cracking behavior of 21Cr2NiMo steel in simulated s
This study aims at providing systematically insights to clarify the impact of cathodic polarization on the stress corros......
Effect of isothermal temper embrittlement and subsequent hydrogen embrittlement on tensile propertie
2.25Cr-1Mo-0.25V base metal (BM) and welded metal (WM) with different temper embrittlement states were obtained by isoth......
Evaluation of hydrogen effect on the fatigue crack growth behavior of medium-Mn steels via in-situ h
Fatigue crack growth(FCG)tests were conducted on a medium-Mn steel annealed at two intercritical annealing temperatures,......
Review of Hydrogen Embrittlement in Metals: Hydrogen Diffusion,Hydrogen Characterization, Hydrogen E
Hydrogen dissolved in metals as a result of internal and external hydrogen can affect the mechanical properties of the m......
Evaluation of Hydrogen Embrittlement Susceptibility of Four Martensitic Advanced High Strength Steel
Martensitic advanced high strength steel(MS-AHSS)belongs to a new class of steels that are currently used in the manufac......
Abnormal Protective Behavior against Hydrogen Permeation of the Corrosion Film Formed on H2S-adjacen
...
Effects of Hydrogen Concentration and Distribution on Hydrogen-induced Cracking in Type 304 Stainles
...
Recently,dissimilar materials welding hasbeen increasingly considered in industry because of its severalbenefits includi......
EFFECT OF BORON MICROALLOYING ELEMENT ON SUSCEPTIBILITY TO HYDROGEN EMBRITTLEMENT IN HIGH STRENGTH M
The susceptibility to hydrogen embrittlement in high strength mooring chain steel with different boron content(0,0.003%,......
Press hardening has become the state-of-art technology in the car body manufacturing to enhance safety standard and to r......
Hydrogen embrittlement of 304L austenitic stainless steel after catholically hydrogen charging: Effe
The effect of plastic pre-deformation on hydrogen embrittlement of 304L austenitic stainless steel was investigated by t......
氢脆具有很强的微观组织敏感性，威胁着各类高强结构材料的安全服役。采用激光-电弧复合焊工艺对BS960E型高强钢进行焊接，并对接头在......
Hydrogen embrittlement of steels is directly linked to hydrogen diffusion and trapping in the microstructure,which can h......
Current Challenges and Opportunities Toward Understanding Hydrogen Embrittlement Mechanisms in Advan
Hydrogen embrittlement (HE) is one of the most dangerous yet most elusive embrittlement problems in metallic materi-als.......
对７０钢卡夹螺旋弹簧的化学成分、金相组织及断口分析表明，其断裂的主要原因是氢脆。其断裂机制属氢致延迟破坏，系弹簧电镀工艺不当所致......
用预充氢方法研究了高合金二次硬化钢２３ＮｉＣｏ不同同火温度的氢脆敏感性，充氢６００回火试样没有影响。４８２℃回火，虽然强度较高，组织中存在的沿马氏体......
堆焊层的表面开裂、氢致剥离，器壁母材的回火脆化、氢脆和氢致裂纹扩展等材质劣化问题是影响热壁加氢反应器的使用安全的主要问题，对......